Abstract
Abstract The present study attempts to tailor the size, morphology and distribution of the ferrite needles/sheaves by thermomechanical processing and develop an ultrafine ferrite + martensite duplex microstructure for enhancement of strength and toughness in SAE 52100 steel. The thermo-mechanical routine included 5% hot deformation before, during or after austenitizing at 950 °C for 15 min followed by austempering at 270 °C for 30 min and subsequent water quenching to room temperature. Optical/electron microscopy along with X-ray diffraction was used to quantitatively monitor the size, morphology and distribution of the phase or phase aggregate. Significant improvement in nanohardness, wear resistance and elastic modulus and was observed in samples subjected to thermomechanical processing, as compared to that following the same austenitizing and austempering routine without hot deformation at any stage. However, improvement in the bulk mechanical property due to the present thermo-mechanical is lower than that obtained in our earlier study comprising cold deformation prior to austenitizing and austempering.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.