Abstract
Cf/ZrB2-SiC ultra-high temperature composites were manufactured via aqueous slurry impregnation coupled with polymer infiltration and pyrolysis, using a allylhydrido polycarbosilane precursor. For the first time we used ultra-high modulus pitch-based carbon fibres for the PIP process, investigating three different architectures, 0/0°, 0/90°, and 2D. Microstructure, mechanical properties and oxidation resistance in air at 1650 °C were investigated. As expected, the mechanical properties showed the tendency to decrease with increase of the preforms complexity, due to the higher amount of flaws and residual stresses. For instance, the flexural strength was approaching 500 MPa for 0/0°, 370 MPa for 0/90° and 190 MPa for 2D. The materials showed an optimal resistance to oxidation at 1650 °C thanks to formation of a viscous borosilicate glass that guaranteed a self-healing functionality.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call