Abstract
ABSTRACT A TiCN-Co-Cr3C2-based cermet, with the addition of 5wt. % and 10wt. %Si3N4 and a reference sample without Si3N4 addition were prepared by the spark plasma sintering technique. The average hardness and fracture toughness of the 90TiCN-5Co-5Cr3C2(SN00) cermet-sintered specimens were e14.85±3.11 GPa and 6.78±0.61 MPaÖm, respectively. The cermet composition 85TiCN-5Co-5Cr3C2-5 wt. % Si3N4(SN05) enhanced the hardness and fracture toughness to 20.90±0.825 GPa and 7.23±0.45 MPaÖm, respectively. Further addition of 10 wt%Si3N4 with 80TiCN-5Co-5Cr3C2(SN10) decreased the hardness value to 16.18±0.279 GPa due to a decrease in the density of defects. However, the fracture toughness steadily increased to 9.34±3.10 MPaÖm. The cermet composition 85TiCN-5Co-5Cr3C2-5Si3N4 (SN05) showed an appreciable improvement in hardness and toughness values due to the formation of a core-rim structure, with the core consisting of TiCN and the rim with TiN, TiO2, TiSi, Co2C, CrN and Cr2Si.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.