MAX phase thin films have been synthesized by thermal treatment of a Ti-Al-C multilayer system. The preparation of the multilayer system was carried out via magnetron sputtering. Based on the thickness ratio among the individual nanoscale monolayers (Ti, Al, C), the resulting MAX phase stoichiometry can be controlled. This paper describes the synthesis of both Ti2AlC and Ti3AlC2 MAX phases from the same precursor multilayer system which is composed of a sequence of Ti/Al/C pure elemental single layers with thicknesses of 14, 6, and 3.5 nm, respectively. This sequence is repeated 22 times with a total thickness of around 500 nm. Rapid thermal treatment tests were performed to study the phase development. The Ti2AlC MAX phase forms in a temperature range below 850 °C, whereas the Ti3AlC2 MAX phase starts to form at temperatures above 850 °C and reaches its highest phase purity at 950 °C. The thin film structures were studied by X-ray diffraction and Raman spectroscopy. Furthermore, the electrical and mechanical properties were investigated to gain more insights regarding the phase transformation and their influence on the thin film properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.