Development of Reactive Ceramics for Conversion of Concentrated Solar Heat Into Solar Hydrogen With Two-Step Water-Splitting Reaction

Abstract

The reactive ceramics suitable for the rotary-type solar reactor (proposed by Tokyo Institute of Technology, Tokyo) with two-step water-splitting reaction were developed. It is confirmed that O2 gas is evolved in the two-step water-splitting reaction with the reactive ceramics vigorously by rapid heating (α-O2-releasing reaction). The α-O2-releasing reaction is due to the formation of interstitial defect and the conversion of lattice oxygen into O2 gas at a nonequilibrium state. Reactive ceramics (NiFe2O4 and yttria stabilized zirconia (YSZ)-NiFe2O4 solid solution) can absorb solar thermal energy and convert thermal energy into chemical energy under high O2 partial pressure atmosphere in the α-O2-releasing reaction. Repetitive evolutions of O2 gas were observed in the two-step water-splitting reaction with YSZ-Fe3O4 solid solution and cerium based metal oxides (CeO2–NiO, CeO2–ZrO2, and CeO2–Ta2O5) at high O2 partial pressure. The CeO2–Ta2O5(Ce:Ta=90:10) released a large amount of O2 gas (3.95 cm3/g) in the α-O2 releasing reaction in the flow of air.