Abstract
AbstractPoly(vinyl acetate) (PVAc) adhesive is often used in the wood industry because it can be rapidly cured at room temperature to produce a high bonding strength. However, PVAc is a linear polymer susceptible to thermal creep, so it will fail to bond in high temperature and humidity environments. In this study, the hot water resistance of PVAc adhesive is improved by introducing lignin with a complex structure to construct multiple cross‐linked networks with a high cross‐link. However, due to the large steric hindrance, the reactivity of lignin hydroxyl groups is low. In the process of preparing adhesive, alkali lignin is hydroxymethylated to improve its reactivity, and then 4,4′‐diphenylmethane diisocyanate is used as a cross‐linker to construct interpenetrating and semi‐interpenetrating polymer networks. The hydroxymethylation occurs through the reaction of formaldehyde with lignin under alkaline conditions. Optimal reaction conditions include a reaction ratio of 0.20, a reaction temperature of 80°C, and a reaction time of 3.5 h. On those conditions, the bonding strength of the lignin‐based PVAc adhesive reaches 1.8 MPa after hot‐water treatment. Therefore, the lignin‐based hot water‐resistant PVAc adhesive has shown good application potential in high temperature and humidity environments.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.