Abstract
Luminescence, scintillation and photoconversion properties of Gd3Al5−x−yScxGayO12:Ce crystals, grown by the micro-pulling-down method, were studied upon substitution of Al for Sc3+ and Ga3+ in the x = 1–2;y = 1–3 ranges. A decrease of the band gap and crystal field strength occurs in these garnets with increasing Sc3+ and Ga3+ content, resulted in blue-shift and reduced thermal stability of Ce3+ emission. Lowering of the scintillation light yield of crystals by two times and scintillation decay kinetic acceleration from 97 to 27 ns is observed at increasing Ga content in the y = 1–3 range. Sc and Ga admixing increases the number of deep charge traps, which additionally deteriorate of crystals scintillation performance. Application of Gd3Al5−x−yScxGayO12:Ce crystals as phosphor converters of white LED was considered. Increasing the Sc3+ and Ga3+ content in crystals leads to linear blue shift of the converter emission and results in increasing the color temperature of LEDs from neutral to could white light.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.