Abstract
A sample with 80 w/o Mg-14 w/o Ni-6 w/o TaF5 composition (named Mg-14Ni-6TaF5) was prepared by reaction-involved milling. The hydrogen absorption and release characteristics of the sample were then investigated. Activation of the sample was finished after two absorption (at 1.2 MPa hydrogen)-desorption (in vacuum) cycles. The activated Mg-14Ni-6TaF5 had a useful hydrogen absorption-desorption capacity approaching 6 w/o at 573 K at 1.2 MPa hydrogen. At 573 K, the activated sample stored 4.98 w/o hydrogen during 5 min, 5.42 w/o hydrogen during 10 min, and 5.74 w/o hydrogen during 60 min at 1.2 MPa hydrogen, and desorbed 0.15 w/o hydrogen during 5 min, 0.37 w/o hydrogen during 10 min, 1.18 w/o hydrogen during 30 min, and 2.22 w/o hydrogen during 60 min at 0.1 MPa hydrogen. The activated sample absorbed hydrogen at a comparatively low temperature of 423 K (3.59 w/o hydrogen in the fifth cycle during 60 min at 1.2 MPa hydrogen). DOI: http://dx.doi.org/10.5755/j01.ms.20.4.6457
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.