Abstract
Glycine nitrate combustion technique was investigated for synthesizing Li(Ni1/3Mn1/3Co1/3-x Na (x) )O-2, x = 0-0.11 based transition metal oxide cathode materials for the rechargeable Li-ion battery (LIB) under this study. X-ray diffraction and scanning electron microscopy analysis showed that the synthesized powder samples were well crystalline rather spherical secondary particles. These secondary particles were composed of softly agglomerated nano-scale primary particles. The room temperature electrical conductivity of these Na-doped materials was significantly higher than that of the base material (2.60 x 10(-7) S/cm). Among them, the x = 0.04 material reported the highest electrical conductivity of 1.02 x 10(-03) S cm(-1). The half-cell assembled with cathode fabricated from Li(Ni1/3Mn1/3Co1/3)O-2 base material showed an initial discharge capacity of 187 mA h(-1) g(-1) with 25 mA h(-1) g(-1) irreversible capacity loss and 88.47% columbic efficiency at C/5 rate with a cut-off voltage of 2.5-4.6 V at 25 A degrees C. The electrochemical behavior of the x = 0.04 cathode showed a comparable initial discharge capacity as of the base material but with improved capacity retention.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.