Abstract
Delayed Hydride Cracking (DHC) is a failure mechanism that occurs in Zr alloys under certain conditions of hydrogen concentration, temperature and stress gradient. In service, hydrogen produced by corrosion reaction can be incorporated in Zr alloys and if the solid solubility is exceeded, hydrogen precipitates as zirconium hydride. The presence of a stress concentrator, such as a crack, generates the hydrogen diffusion and precipitation to the high stress zone beginning the DHC process. In this work, in-situ DHC tests in air at 250°C were performed at ANTARES, the neutron imaging facility of the FRM-II reactor. Samples of Zr2.5%Nb produced from extruded tubes and pressure tubes were studied using a stress rig specially modified to perform DHC tests in the neutron beam. H redistribution during mechanical testing was followed in-situ by registering the changes in neutron transmission. The results were compared with the images obtained by light optical microscopy after the tests. The results highlight the capabilities of neutron imaging to analyze time-dependent H distribution during DHC crack growth.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.