Abstract
The effects of V substitution for Cr to the sintering behavior of Cr containing Mo2NiB2 ternary boride base cermets and Mn addition to the mechanical properties and microstructure of the Cr and V containing cermets were investigated by using Ni-5.0B-51.0Mo-(17.5-x)Cr-xV (mass%) and Ni-5.0B-51.0Mo-12.5Cr-5.0V-(0-1.5)Mn (mass%) model cermets. 10mass%V substitution for Cr in the Cr containing cermets markedly improved transverse rupture strength and hardness from 2.27 to 2.94GPa and from 85.3 to 87.2RA respectively and refined the microstructure by retarding the progress of sintering especially at liquid phase sintering stage. Small amount of Mn addition to the Cr and V containing Mo2NiB2 base cermets significantly improved the sinterability and increased the mechanical properties of the cermets.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.