Abstract
Homogeneous and ultrafine eutectic like microstructures without coarse primary crystals were formed by a crystallisation of amorphous phases for several rare earth (RE) oxide–Al2O3 eutectic systems with the off eutectic compositions. Mixtures of RE oxide and Al2O3 powders with the off eutectic compositions were melted and quenched rapidly to form the amorphous phases. A heat treatment of the amorphous phases at 1000 and 1300°C for 30 min formed RE3Al5O12/Al2O3 (or REAlO3/Al2O3) phases. This method utilises a low migration rate in the amorphous phases. SEM observation of these materials heat treated at 1300°C showed homogeneous eutectic like microstructures. Formation of primary crystals, which are always formed in the ordinal off eutectic microstructure, was absolutely suppressed. Furthermore, the microstructures were much finer than those of materials ordinarily prepared from eutectic melts.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.