Abstract
This study was carried out on the development of the evaluation method for solidification cracking susceptibility of Inconel600/SUS347 dissimilar weld metals during laser welding. Some dissimilar weld metals which have different ratios of Inconel600/SUS347 were prepared by TIG welding and then were remelted on the U-type hot cracking tester by laser. Solidification cracking behavior during hot cracking test was observed by a high speed camera and the dynamic strain, close to the solidification crack, was evaluated. It appeared that local critical strain, for the initiation of solidification crack, was obtained by this strain measurement method. So the solidification cracking susceptibility could be directly evaluated based on the critical strain for different dissimilar joint. By using this method, it was discovered that solidification cracking occurred most easily when the ratio of Inconel600/SUS347 is 40%/60%, in the case of the Inconel600/SUS347 dissimilar laser welded joints.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.