Abstract

Abstract To reduce the use of noble metals, iridium oxide (IrO2) catalysts are prepared on carbon paper (CP) by electrodeposition for use as the anodes in polymer electrolyte membrane water electrolysis (PEMWE). The activities of the fabricated electrodes toward the oxygen evolution reaction are evaluated. The loading amount and morphology of the IrO2 deposits are varied by controlling the electrodeposition potential (Edep) and time (tdep). When electrodeposited at 0.7 V, the IrO2 loading ranges from 0.007 to 0.464 mg cm−2 (tdep: 1 ∼ 30 min). In the PEMWE test at 90 °C, the IrO2/CP electrode with an IrO2 loading of 0.1 mg cm−2 shows the highest performance (1.92 A cm−2 at 1.8 V) in which high IrO2 utilization is achieved without significant exposure of the substrate carbon surface. The developed IrO2/CP electrodes provide cell performances comparable to those in previous reports with a higher IrO2 loading, indicating markedly enhanced mass activity.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.