Abstract
Ni deposited on HA powder was prepared by electroless plating process without sensitization and activation treatment. The deposited powder obtained was characterized by energy dispersive spectroscopy (EDX) and x-ray diffraction (XRD). The microstructure and hardness of the sintered powder were examined by scanning electron microscopy (SEM) and Vickers hardness respectively. From the result, the nickel existence in the deposition was confirmed by the EDX analysis. The diffraction peaks at 44.5 and 64.7o (2θ) of planes (111) and (211) respectively were belong to nickel. Nickel are homogeneously dispersed in HA matrix with grain size between 0.25-2μm after sintered at 1250°C. The improvement of 93% and 180% in average hardness and flexural strength respectively were achieved with nickel presence in HA compared to pure HA.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.