Abstract
The article discusses the results of investigations performed during a thermo-mechanical treatment of forgings made of chromium‑molybdenum 42CrMo4 grade steel. The treatment was realized during a regular series production. The forging process was combined with a heat treatment carried out directly after forging on a specially adapted station. Such a production technology will make it possible to eliminate the step of repeated heating of the forgings. On the example of an element of a steering gear, it was demonstrated how it is possible to perform an isothermal annealing process starting from the temperature at which the trimming of the forgings ends. During the cooling of the forgings, it is enough to maintain the temperature at the proper level in order for the exothermal phase transformation of austenite into pearlite to take place. The test results show that, with the properly selected temperature of isothermal annealing, it is possible to obtain an equilibrial ferritic-pearlitic structure in the required hardness scope. Introducing such a solution into the industrial practice would allow savings more than 80% of the energy used for the heat treatment of forging in this case.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.