Abstract
Weight reduction is often considered the primary goal in the development of structure materials. A new Ti-8Al-1Cr-1V-0.5Fe-0.1Si (wt.%) alloy with a low-density and a high-strength was developed in this work. The microstructures and mechanical properties of the alloy were investigated in hot-rolled and solution-aging (STA) treatment conditions. The microstructures of the alloy in both states consist of the spherical αp phase, acicular αs phase, and a small amount of β phase. Attributed to such heterogeneous microstructures, the hot-rolled alloy exhibits an outstanding tensile strength of 1046.1 MPa, a total elongation of ~8.3%, and an impressive low density of 4.23 g/cm3. After heat treatment, the alloy also exhibits a similar strength and ductility. A detailed analysis of the deformation modes shows that the numerous dislocations slippages and deformation twinning in the αp phase are the main reasons for the high ductility, and the acicular αs phase provides the alloy with high strength after heat treatment. This newly developed alloy is a potential material for various structural applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.