Abstract
Accumulative roll bonding (ARB) process have been used develop Mg-2%Zn/Ce/Al hybrid composite and microstructure, mechanical and corrosion properties were investigated. The electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) revealed that the grains are significantly reduced and reaches up to 1 μm in Mg-2%Zn layer and 1.8 μm in Al layer having high angle misorientation of grain boundaries after subjected to 5-passes of the ARB process. The Al17Mg12, AlMg4Zn11 and Al11Ce3 intermetallic phases were observed through the XRD analysis. Mechanical properties of the hybrid composite improved with increase in the number of ARB passes which is attributed to work hardening, grain refinement and uniform distribution of Ce particles. Presence of Ce in the hybrid composite restricts the phenomenon of dynamic recrystallization and prevents the grain growth during ARB process. The corrosion rate of Mg-Zn/Ce/Al hybrid composite (0.72 mm/y) improved about 3.3 times as compared to that of Mg-2%Zn alloy (2.37 mm/y).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.