Abstract
Tritium permeation through structural materials is a critical issue in fusion reactors from the viewpoints of sufficient fuel balance and radiological hazard. Ceramic coatings have been investigated as tritium permeation barrier for several decades; however, irradiation effects of the coatings on permeation are not elucidated. In this work, yttrium oxide coatings were fabricated on reduced activation ferritic/martensitic steels by radio frequency magnetron sputtering, and their microstructures and deuterium permeation behaviors were investigated before and after iron-ion irradiation at different temperatures. An as-deposited coating had a columnar structure and transformed into a granular one after annealing. An amorphous layer formed near the coating-substrate interface of irradiated coatings, and its thickness became thinner with increasing irradiation temperature. Voids of approximately 20 nm in diameter also formed in the irradiated coatings. Deuterium permeation flux of the sample irradiated to 1 dpa at room temperature was the lowest among the unirradiated and irradiated samples, and a permeation reduction factor indicated up to 390. The amorphous layer disappeared after deuterium permeation measurements due to damage recovery, while the voids remained and aggregated. The irradiation damage would accelerate nucleation of the crystal, resulting in a decrease of the permeation flux.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.