Abstract
Retrospective dosimetry was used to determine the accumulated neutron exposure of AISI 304 stainless steel removed from the top guide of a boiling water reactor located at the Oyster Creek nuclear power station. The material was removed from areas adjacent to cracks that were observed after ∼20 years of operation. Using the plant operational history and a variety of measurements of various radioisotopes or non-radioactive transmutation products produced by irradiation, it was possible to determine the integrated neutron fluence experienced by the cracked region and to specify the accumulated displacement dose. Dose estimates on two separate specimens adjacent to the cracks were found to average 1.5 ± 0.2 dpa, possibly reflecting some uncertainty in measurement but more likely suggesting a small gradient in neutron flux-spectra within the section from which the various analysis specimens were cut. This report demonstrates that it is possible to examine defective components lying outside of the core region and where neutron flux-spectra are not well known, and to use the induced transmutation products to determine the neutron exposure with some confidence by using the examined specimen as its own dosimeter.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.