Abstract
The polarity of the lattice of bulk single GaN crystals and the polarity of homoepitaxial and heteroepitaxial-on-sapphire GaN thin films has been studied using convergent beam electron diffraction. Diffraction patterns obtained at 200 kV for the 〈1–100〉 projection of GaN were matched with calculated patterns. The lattice orientations of two commonly observed bulk single-crystal facets were identified. It is shown that the smooth facets in single crystals correspond to the (0001), Ga-terminated, lattice planes, whereas the rough facets correspond to the (0001̄), N-terminated, planes. It is also shown that metalorganic chemical vapor deposition epitaxy retains the polarity of the substrate, i.e., no inversion boundaries were observed. Heteroepitaxy on sapphire is shown to grow in the (0001), Ga-terminated orientation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.