Abstract
AbstractThe intrinsic lateral sonic moduli of the crystalline and amorphous regions of poly(trimethylene terephthalate) (3GT) (about 4.1504 ± 0.8396 GPa and 1.6096 ± 0.0368 GPa, respectively) were obtained from sonic moduli and crystallinities of unoriented 3GT filaments annealed under different conditions. Using the obtained intrinsic lateral sonic moduli of the crystalline and amorphous regions, the degree of orientation of the amorphous region of uniaxially drawn 3GT filaments could also be obtained from the crystallinity, sonic modulus, and the degree of crystalline orientation estimated from X‐ray azimuthal scan data. Thus, the intrinsic birefringences of the perfectly oriented crystalline and amorphous regions of the 3GT fibre (about 0.2057 ± 0.0160 and 0.2175 ± 0.0923, respectively) could be obtained from the appropriate combinations of birefringence, crystallinity, and the degree of orientation of the crystalline and amorphous regions.© 2003 Society of Chemical Industry
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.