Abstract
The phenomena of pile-up and sink-in associated with nanoindentation have been found to have large effects on the measurements of the indentation modulus and hardness of copper. Pile-up (or sink-in) leads to contact areas that are greater than (or less than) the cross-sectional area of the indenter at a given depth. These effects lead to errors in the absolute measurement of mechanical properties by nanoindentation. To account for these effects, a new method of indenter tip shape calibration has been developed; it is based on measurements of contact compliance as well as direct SEM observations and measurements of the areas of large indentations. Application of this calibration technique to strain-hardened (pile-up) and annealed (sink-in) copper leads to a unique tip shape calibration for the diamond indenter itself, as well as to a material parameter, a, which characterizes the extent of pile-up or sink-in. Thus the shape of the indenter tip and nature of the material response are separated in this calibration method. Using this approach, it is possible to make accurate absolute measurements of hardness and indentation modulus by nanoindentation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.