Steel bars in reinforced concrete (RC) structures may corrode in an aggressive environment, resulting in performance deterioration and premature failure. Stirrups begin to corrode earlier and faster than longitudinal steel bars due to their thinner concrete cover, and the shear strength decreases faster than the flexural strength. This paper presents an experimental investigation into the deterioration mechanism of shear behavior for corroded RC beams, and the prominent influencing parameters on shear behavior. The impressed current method was used to obtain corroded RC beams with different corrosion degrees in stirrups and longitudinal steel bars. Test results indicated that the beam may fail in shear instead of bending as the degrees of stirrup corrosion increases. The more severe the corrosion of stirrups was, the lower the shear strength. However, as the degree of corrosion increased in the longitudinal steel bars, the failure mode could change back to bending failure. The loss of bond strength affected the shear behavior of corroded RC beams, and the shear strength for bonded specimens was larger than unbonded ones. The shear strength decreased in beams with stirrups lacking end anchorages. Stirrups without end anchorages could still contribute to the shear strength if there was a good bond between stirrups and concrete. Otherwise, the stirrups could be ignored. With neither bond strength nor end anchorage, the beam could be treated as a beam without stirrups.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.