Abstract
The corrosion performances of the as-cast and solution-treated Mg-0.5Zn samples were investigated in 0.9% NaCl solution and compared. From the electrochemical measurement results and corrosion morphology observations, it is found that the corrosion resistance of Mg-0.5Zn deteriorated with the extension of solution treatment duration. The main reason was the formation of Fe-Si precipitates with higher Fe concentrations during heat treatment. The Fe-Si precipitates, especially the ones with high Fe contents influenced the corrosion initiation and propagation significantly. In regard of corrosion performance, the solution-treated and then extruded sample was also performing not as good as the cast and then directly extruded sample.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.