Abstract
The stress corrosion crack (SCC) of 304 nuclear grade (NG) stainless steel (SS) in 0.5 mol/L NaCl+1.5 mol/L H2SO4 was monitored using electrochemical noise (EN) based on chaos theory, statistics and wavelet analysis. The results indicated that the SCC process was divided into three stages according to the transient features in the EN. In the beginning, compared with the sample without applied stress, the enhanced fluctuation amplitude in the electrochemical current noise (ECN) of the stressed samples was attributed to stress-enhanced pitting corrosion and uniform corrosion; then the fluctuations of ECN for all the samples decreased due to a coverage by the corrosion products; however, the ECN fluctuations of stressed sample were larger than the unstressed sample, suggesting that the stress enhanced the SCC initiation and propagation. Chaos analysis revealed that the correlation dimensions increase from 2.1 to 2.5 during the corrosion process, and the applied stress seems increase the complexity and uncertainty of the ECN signal.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.