Abstract
Detecting mechanical fatigue of metallic components is always a challenge in industries. In this work, we proposed to monitor the low-cycle fatigue of a 6061 aluminum alloy based on internal friction (IF) measurement, which is realized by a quantitative electromechanical impedance (Q-EMI) method using a small piezoelectric wafer bonded on the specimen. Large stress amplitude (230 MPa) was employed in the testing; thus, the fatigue life can always be below 105 cycles. It was found that except for the initial testing stage, the IF always increases steadily with the increasing fatigue cycles. Before the fatigue failure, the IF can reach 2.5–3.4 times the initial value, which is thought to be caused by the micro-cracks forming and growing. In comparison, the resonance frequency of the specimen just drops by about 2% compared with the initial value. Finally, a fatigue criterion based on IF measurement is suggested for aluminum alloys and it can also be extended to other metals.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.