Abstract
ABSTRACTTwo different TiO2 compact films, fabricated by sol-gel spin-coating (SC) and spray-pyrolysis (SP) processes, were employed as an electron transport layer (ETL) to the nanostructured hybrid perovskite solar cells (PSCs), and they were comprehensively investigated through the various characterisation approaches using electrochemical and physicochemical approaches. With cyclic voltammetry and XPS results, the absence of pinholes on the SP-TiO2 compact films was indicated, and AFM and SEM results confirmed the SP-TiO2 compact films had lower surface roughness and more compact particle connectivity, offering a decent interface between the perovskite active layer and the adjacent TiO2 films. The performance of the SP-PSCs using the SP-TiO2 compact films was 7.06%, which was 3 times higher than that of the SC-PSCs. Voc decay measurement also confirmed that such pinhole-free and improved film interfaces of SP-TiO2 compact films contributed to elongating electron lifetime in PSCs by the enhanced hole blocking effect of the SP-TiO2 compact films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.