Design of a new nanocomposite between bismuth nanoparticles and graphene oxide for development of electrochemical sensors

Abstract

This study describes a new route for preparation of a nanocomposite between graphene oxide (GO) and bismuth nanoparticles (BiNPs) and its evaluation as modifier electrode for development of electrochemical sensors. BiNPs were synthesized under ultrasound conditions using Bi(NO3)3 as metal precursor and ascorbic acid (AA) as reducing agent/passivating. Some experimental parameters of BiNPs synthesis such as Bi3+:AA molar ratio and reaction time were conducted aiming the best voltammetric performance of the sensor. Glassy carbon electrodes (GCE) were modified by drop-casting with the BiNPs dispersions and anodic stripping voltammetry measurements were performed and revealed an improvement in the sensitivityfor determination of Cd(II) and Pb(II) compared to an unmodified electrode. The best electrochemical response was obtained for a BiNPs synthesis with Bi3+:AA molar ratio of 1:6 and reaction time of 10min, which yielded Bi metallic nanoparticles with average size of 5.4nm confirmed by XRD and TEM images, respectively. GO was produced by graphite oxidation using potassium permanganate and exfoliated with an ultrasound tip. GO-BiNPs nanocomposite was obtained by a simple mixture of GO and BiNPs dispersions in water and kept under ultrasonic bath for 1h. GCE were modified with a nanocomposite suspension containing 0.3 and 1.5mgmL−1 of GO and BiNPs in water, respectively. Under optimized conditions, the proposed nanocomposite was evaluated on the voltammetric determination of Pb (II) and Cd (II), leading to a linear response range between 0.1 and 1.4μmolL−1 for both cations, with limit of detection of 30 and 27nmolL−1, respectively. These results indicate the great potential of the GO-BiNPs nanocomposite for improving the sensitivity of voltammetric procedures.