Abstract
Coating degradation is a critical issue when steel surfaces are subject to weathering. This paper presents a chipless, passive antenna tag, which can be applied onto organically coated steel. Simulations indicated that changes associated with organic coating degradation, such as the formation of defects and electrolyte uptake, produced changes in the backscattered radar cross section tag response. This may be used to determine the condition of the organic coating. Simulating multiple aging effects simultaneously produced a linear reduction in tag resonant frequency, suggesting coating monitoring and lifetime estimation may be possible via this method. For coatings thinner than calculations would suggest to be optimum, it was found that the simulated response could be improved by the use of a thin substrate between the coated sample and the antenna without vastly affecting results. Experimental results showed that changes to the dielectric properties of the coating through both the uptake of water and chemical degradation were detected through changes in the resonant frequency.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.