Abstract

A new structure-directing agent, hexadecyl-2-pyridinyl-methylamine, L16, was prepared through Schiff base condensation between pyridine-2-carboxaldehyde and hexadecylamine followed by reduction of the imine with NaBH4. Mesoporous and supermicroporous tin oxide particles with crystalline pore walls were obtained through a low-temperature sol–gel synthesis process by using an anionic surfactant, sodium dodecylsulfate, and hexadecyl-2-pyridinyl-methylamine, respectively, as templates. Powder X-ray diffraction, transmission electron microscopy−energy-dispersive spectrometry, field emission scanning electron microscopy, CHN chemical analysis, N2 sorption, 1H and 13C NMR, high-resolution mass spectrometry, Fourier transform infrared spectroscopy, and UV–vis absorption spectroscopic tools were employed to characterize L16 and nanostructured SnO2 materials. X-ray diffraction and transmission electron microscopy image analyses suggested that these porous materials have a wormhole-like disordered arrangement of pores, whereas the pore walls are crystalline. Nitrogen physisorption studies show high specific surface areas up to 555 m2 g−1, and the uniform nanoscale pore size distribution ranged from supermicropore to mesopores for these materials. These SnO2 materials showed drastic reduction of dielectrics with the induction of porosity vis-à-vis bulk SnO2. These unique optical and electrical properties of porous SnO2 materials over bulk SnO2 could be attributed to the quantum confinement effect.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call