Abstract
In situ Ti2AlC/TiAl composite was first fabricated by reactive hot-pressing technique at low temperature of 1150°C for 2 h using Ti3AlC2 and Ti–Al alloy powders. The composite with fine-grained structure consisted of TiAl, Ti3Al and Ti2AlC phases. The Vickers hardness, flexural strength and fracture toughness of the Ti2AlC/TiAl composite reached 5.2 GPa, 937.7 MPa and 7.7 MPa m1/2, respectively. The action mechanism for the composite was mainly attributed to the grain refinement, the uniform distribution of the dispersed Ti2AlC particles, transgranular cracking, crack deflection, crack bridging and pull-out of Ti2AlC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.