Abstract
Surface machining processes are responsible for creating microstructures that reside near the surfaces of a substrate and are characterized by the fabrication of micromechanical structures from deposited thin films. These films can be selectively removed to build three-dimensional structures whose functionality typically requires that they should be freed from the planar substrate. Silicon nitride thin film is one of these important materials. In this paper, by adjusting the SiH2Cl2/NH3gaseous ratio, low stress silicon nitride (LS SiN) is deposited by the low pressure chemical vapor deposition (LPCVD) process. The internal stress generally in 135 MPa has been detected using an FLX-2320 film stress tester. Based on the wide application in surface micromachining devices, the mechanical properties of LS SiN are measured by nanoindentation, giving the value of Young’s modulus of 224 GPa and the hardness of 22.5 GPa, respectively. Dry etching and wet etching are utilized to fabricate the LS SiN thin film for structural layers. The etching rate compared with normal Si3N4film by LPCVD is demonstrated for silicon chip manufacture.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.