Dependence of the tensile properties of 316 L parent material and welds on implanted hydrogen and/or helium

Abstract

Abstract The interest in the low temperature tensile properties of candidate alloys for first wall and blanket structures of future fusion devices is due to the possible low pressure water cooling and the associated low operation temperature in recent design studies. Therefore, the tensile properties of hydrogen and/or helium implanted 316 L stainless steel and its weldments as a function of gas concentrations and temperature were investigated. The main effects of the implantation are hardening, resulting in large increases of the yield strength proportional to the implanted gas concentration, and a gradual decrease of the corresponding rupture strain. The ultimate tensile stresses are less affected. The effect of helium implantation seems to be more pronounced than that of hydrogen implantation. At 673 K most of the implantation induced changes are recovered. Generally parent material and welds still show large ductility (≥20%) under all conditions investigated.