Abstract
Abstract Antiphase boundaries are examined in an L12 structure, with particular attention paid to those that result from dissociation via a glide or a climb process of a superlattice dislocation with an a〈110〉 Burgers vector. In the case of a climb dissociation process, emphasis is placed on those antiphase boundaries which could exhibit local deviations from the stoichiometric composition A3B. The antiphase boundary energies are computed for a number of plane orientations so as to leave no region of the stereographic projection unexplored. A set of empirical potentials representing mechanically stable L12 alloys with different glide antiphase boundary energies on {001} and {111} and two distinct anisotropy ratios are used. It is found that the main effect of atomic relaxation is to significantly reduce the amplitude of the antiphase boundary energy variations with orientation: given the a/2[110] displacement vector, the low antiphase boundary energy on (001) is practically unaffected, whereas the high an...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have