Abstract
Single crystal Gd 2 Si 2 O 7 :Ce (GPS:Ce) scintillators were grown by a top seeded solution growth (TSSG) method and their crystal structures and scintillation properties were measured. Single crystal GPS with several cerium concentration; (Gd 1‒x Ce x ) 2 Si 2 O 7 (x=0.025, 0.1, 0.15), were synthesized with a RF-Czochralski furnace. For GPS:Ce 2.5 at.%, a crystal structure was orthorhombic. For GPS:Ce 10 and 15 at.%, these were triclinic. In PL measurements, broad emissions around 350 to 450 nm correspond to 5d–4f transitions of Ce3+ were observed. In gamma-ray measurements, each scintillator shows light output larger than that of BGO. High energy resolution of around 5% was obtained for GPS:Ce 2.5 and 10 at.%. GPS:Ce 2.5 at.% shows ca. 4.4 times light output larger than that of BGO. Decay times of triclinic GPS were faster than that of orthorhombic GPS.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.