Dependence of Annealing Temperature on the Conductivity Changes of ZnO and MgZnO Nanoparticle Thin Films from Annealing in a Hydrogen Atmosphere at Mild Temperatures

Abstract

ABSTRACTWe report apparent robust doping of ZnO and MgxZn1-xO (x ∼20%) nanoparticle films by annealing in hydrogen gas. The annealing was done at sequentially higher temperatures from about 20 °C to 140 °C. The effect of the annealing was determined by comparing current-voltage measurements of the samples at room-temperature and in vacuum after each annealing cycle.The nanoparticles were grown using an aqueous solution and heating process that created thinfilms of ZnO or MgZnO nanoparticles with diameters of about 30 nm. When exposed to hydrogen gas at room-temperature or after annealing at temperatures up to about 100 °C, no measureable changes to the room-temperature vacuum conductivity of the films was observed. However, when the samples were annealed at temperatures above 100 °C, an appreciable robust increase in the room-temperature conductance in vacuum occurred. Annealing at the maximum temperature (∼135-140 °C) resulted in about a factor of about twenty increase in the conductivity. Furthermore, the ratio of the conductance of the ZnO and MgZnO nanoparticle films while being annealed to their conductance at room-temperature were found to increase and then decrease for increasing annealing temperatures. Maximum changes of about five-fold and seven-fold for the MgZnO and ZnO samples, respectively, were found to occur at temperatures just below the annealing temperature threshold for the onset of the robust hydrogen gas doping. Comparisons of these results to other work on bulk ZnO and MgZnO films and reasons for this behavior will be discussed.