Abstract
The kinetics of structural relaxation in a Pd40Ni40P20 bulk metallic glass was investigated by the volume relaxation due to density experiments and the enthalpy relaxation due to specific heat experiments. A two-step relaxation process was found in the volume relaxation, while the enthalpy relaxation seemed to be one-step relaxation process with a spectrum of relaxation times. First-step volume relaxation only in as-quenched glass was the process with a spread of relaxation times at lower relaxing temperature, while a Debye-type relaxation behavior was observed at higher temperature near Tg and in pre-annealed glass. The comparison of the kinetics of volume and enthalpy relaxations at the same temperature showed a disagreement with the prediction of free volume theory.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.