Abstract
Sintered bulks of commercial ZrO2 nanopowders were produced by combined application of magnetic pulsed compaction (MPC) and subsequent two-step sintering, and finally, their density, hardness, shrinkage and formability were analyzed. The formability tests were conducted by a CAD/CAM system. Nearly fully dense (∼98%) commercial ZrO2 bulks were successfully obtained. With increasing MPC pressure, there was a decrease in the grain size of zirconia block. The ratio of PVA did not have a remarkable effect on the grain size. The optimum compaction pressure during MPC was 1 GPa and mixing conditions included using 1.0 wt. % PVA. The optimum processing condition included MPC process, followed by two-step sintering (first at 1000 and then at 1450 °C). The bulk under these conditions was found to have good formability, ∼97% density, reasonable hardness (1150 Hv) and ∼19% shrinkage.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.