Abstract
β-SiAlON–cubic boron nitride (cBN) composites were prepared from β-SiAlON and cBN powders at 1600°–1900°C under a pressure of 100 MPa by spark plasma sintering. The effects of cBN content and sintering temperature on densification and phase transformation of the β-SiAlON–cBN composites were studied. When 10–30 vol% cBN was added to β-SiAlON, the shrinkage rate of the compacts increased. The compacts of β-SiAlON–BN composites originally containing 10–30 vol% cBN ceased to shrink at a temperature lower than that of β-SiAlON and the density of the composites increased. The densification of β-SiAlON–BN composites originally containing >40 vol% cBN was suppressed. The phase transformation of cBN to hexagonal BN in the β-SiAlON–BN composite was inhibited to a greater degree than that in the cBN body.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.