Abstract
Mould casting and drop-tube techniques were used to solidify a AlCoCrFeNi2.1 eutectic high-entropy alloy under conditions of high cooling rate. The samples obtained from two different methods present the same phase constituent, FCC and B2 phases. During mould casting experiments the alloy almost solidified into the eutectic structure consisting of lamellar and anomalous morphology, with a tiny fraction of cellular and dendrite morphology being observed at certain sites of the sample surface due to the corresponding high cooling rate. Instead, during drop-tube experiments a typical, coarse dendrite structure of FCC single phase was formed across the entire 106-150 μm particle. The cellular structure can also be formed directly from the melt. The rest region solidified into the general eutectic morphology as was observed in the casting rods. The results clearly indicate the transition from coupled eutectic growth to single-phase dendrite growth with increasing departures from equilibrium for the multi-component AlCoCrFeNi2.1 eutectic high-entropy alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.