Abstract
Al0.4Ga0.6N/Al0.65Ga0.35N heterojunction phototransistors have been fabricated from the epi-structure grown by low-pressure metal organic chemical vapor deposition on c-plane sapphire substrates. P-type conductivity of the AlGaN base layer was realized by using indium surfactant-assisted Mg-delta doping method. Regrowth technique was used to suppress the Mg memory effect on the n-type emitter. The fabricated devices with a 150-μm-diameter active area exhibited a bandpass spectral response between 235 and 285 nm. Dark current was measured to be less than 10 pA for bias voltages below 2.0 V. A high optical gain of 1.9 × 103 was obtained at 6 V bias.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.