Abstract
It is very imperative to improve delayed fracture properties of high strength steel, which may enlarge its usage. The published literature shows that the susceptibility to hydrogen embrittlement of a novel 1 500 MPa bainite/martensite dual-phase high strength steel is inferior to that of conventional quench-tempered high strength steel. The stress corrosion cracking (SCC) in a 3.5% NaCl solution for novel 1 500 MPa bainite/ martensite dual-phase high strength steel was investigated in this paper by using modified wedge-opening-loading (WOL) specimens. The experimental results show that KISCC for novel 1 500 MPa bainite/martensite dual-phase high strength steel is larger than 50 MPa·m1/2, exceeding conventional high strength steel. Its crack growth rate (da/dt)II is about 1×10−5 mm/s, which is less than that of conventional high strength steel. Hydrogen trapping phenomena in the steel were investigated by electrochemical permeation technique. The lath boundaries and stable retained austenite are beneficial hydrogen trap, slowing down the segregation of hydrogen on the crack tip, hence KISCC increases and crack growth rate decreases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call