Abstract
Delamination cracking in thermal barrier coating (TBC) system is studied with the newly developed theoretical model. A semi-infinite long interface crack is pre-existing. The thermal stress and temperature gradient in TBC system are designated by a membrane stress P and a bending moment M. In this case, the effects of plastic deformation, creep of ceramic coating, as well as thermal growth oxidation and temperature gradient in TBC system are considered in the model due to the fact that these effects are considered in the calculation of thermal stress. The energy release rate, mode I and mode II stress intensity factors, as well as mode mixed measure ψ, are derived. The emphatic discussion about PSZ/Ni-alloy reveals that the TBC system may not fail in the form of coating delamination during the period of heat hold. However, the failure may be in the form of coating delamination during cooling or in the heating period during the second cycle or later cycles. The conclusion is consistent with the experimental observations. The delamination of ceramic coating is induced by the compressive load in the coating.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.