Abstract
AlH3 is a promising hydrogen storage material due to its high hydrogen capacity (10 wt%) and relatively low dehydriding temperature. In this work, γ-AlH3 was prepared by organometallic synthesis method and the effects of ball milling on dehydriding properties of γ-AlH3 were investigated systematically. Experimental results shows that as-prepared γ-AlH3 releases about 8.3 wt% of hydrogen in the temperature range of 130–160 °C at a heating rate of 2 °C/min. Ball milling significantly improves the dehydriding behavior of γ-AlH3. DSC-MS analysis reveals that the dehydriding temperature of γ-AlH3 ball-milled for 10 h decreases by around 30 °C. In addition, the dehydriding activation energy of γ-AlH3 ball-milled for 2 h decreased from 87 to 68 kJ/mol. Isothermal dehydriding measurements demonstrate that duration needed to release 90% hydrogen for as-prepared γ-AlH3 is 280 min, but it takes only 82 min after ball milled for 10 h to release the same amount of hydrogen. Moreover, the dehydriding path of γ-AlH3 is changed by ball milling. As-prepared γ-AlH3 transforms to α-AlH3 before dehydriding, while ball-milled γ-AlH3 prefers to dehydride directly without firstly transforming to α-AlH3.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.