Abstract
The interfacial reaction between electroless Ni(P) under-bump metallization (UBM) and solders is studied. A P-rich layer forms in the UBM along the solder side after reflow and thermal aging. Crack formation inside the P-rich layer can sometimes penetrate throughout the entire UBM layer structure. The Ni(P) UBM degradation occurs earlier in the Sn3.5Ag solder than in Sn37Pb because of its higher reflow temperature. Despite the formation of a P-rich layer and cracks inside the UBM, it still keeps its original function within the high-temperature storage period in this study. Explanations for the formation of the P-rich layer and cracks in the UBM are outlined along with explanations for the Ni(P) UBM degradation process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.