Abstract
In order to improve the corrosion resistance of metallic materials in molten zinc, ZrO2–Ni/Al gradient coatings were sprayed on the surface of the Fe–0.35–0.44 wt.% C steel. The corrosion behaviour and corrosion mechanism of the ZrO2–Ni/Al gradient coatings in molten zinc were studied. The ZrO2–Ni/Al gradient coatings on the surface of steels prolonged the lifetime of samples and changed the corrosion behaviour of the samples in molten zinc. The lifetime of the ZrO2–Ni/Al gradient coatings immersed in molten zinc at 620 °C is 28 days, which is 4 times as long as that of the general ZrO2 coatings. The ZrO2–Ni/Al gradient coatings were corroded in molten zinc at 620 °C, which was caused by zinc atom diffusing along the crystal boundary and pores of the ZrO2–Ni/Al gradient coatings, and reacting with Ni/Al particle in the ZrO2–Ni/Al gradient coatings. The corrosion mechanism of the coatings in molten zinc at 620 °C was crystal boundary corrosion, pitting corrosion and reaction corrosion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.