Abstract
For the first time, the preparation of doubly porous “poly(ε-caprolactone)-like” networks through free-radical ring-opening copolymerization of 2-methylene-1,3-dioxepane with divinyl adipate was achieved via a double porogen templating approach. This versatile strategy allowed for the formation of macropores of around 150 μm generated by removal of sieved and sintered NaCl particles in water, while smaller pores in the 1–10 μm range were created by phase separation during the copolymerization process through a syneresis mechanism in the presence of a porogenic solvent. The chemical nature of the as-obtained scaffolds was evidenced by Raman spectroscopy. The two distinct porosity levels could be examined by scanning electron microscopy and mercury intrusion porosimetry. The nature of the porogenic solvent as well as its volume proportion and the amount of crosslinking agent in the polymerization feed allowed for finely tuning the porous features of the micropores. The crucial role of the double porosity of such biporous scaffolds on their water uptake and mechanical properties under compression was assessed by comparing them with their monoporous analogues, while their degradability was investigated in different alkaline aqueous media. The double porosity enabled a synergistic effect regarding the water uptake of the resulting scaffolds when compared to their monoporous counterparts. Doubly porous polymeric materials with appropriate mechanical properties were obtained, possessing high compressibility and shape memory behavior upon consecutive compression cycles. Finally, these materials display degradation rates that could be controlled depending on medium pH.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.