Abstract
Neutron powder diffraction and temperature dependent dielectric studies were carried out on Ca-substituted Na0.5Bi0.5TiO3, i.e., (Na0.5Bi0.5)1−xCaxTiO3. Stabilization of an orthorhombic phase even at a low Ca concentration (0.05<x≤0.10) suggests that Na0.5Bi0.5TiO3 (NBT) is susceptible to orthorhombic distortion. The orthorhombic and rhombohedral phases coexist for x=0.10, suggesting these phases to be nearly degenerate. The orthorhombic distortion favoring tendency of Ca assists in promoting the inherent instability with regard to this structure in pure NBT, which was reported recently.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.