Hydrogen can dissolve to a significant extent in molten aluminium and is the main cause of gas porosity in castings. The effect of intensive melt shearing on hydrogen concentration in molten aluminium alloy has been studied by both reduced pressure test and direct hydrogen measurement, and the results show that intensive melt shearing has a significant degassing effect for the LM24 aluminium alloy melt. By applying intensive melt shearing, the hydrogen concentration in the liquid alloy was reduced from 0·16 to 0·08 mL/100 g, and the density index Di was reduced from 12·40 to 2·96%. It was also found that shearing speed, shearing time and holding time after shearing could influence the degassing efficiency. In addition, pressurised melt filtration was also carried out to understand the mechanism of reduced porosity by intensive melt shearing, particularly the role of oxide in the formation of porosity, and the microstructure refinement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.